报告题目：超硬 (MoSiTiVZr)Nx 高熵氮化物涂层
Superhard (MoSiTiVZr)Nx high-entropy nitride coatings
报告内容简介：本报告介绍了高熵合金涂层的研究背景和当前进展，重点探讨了(MoSiTiVZr)Nx高熵氮化物涂层。研究表明，随着氮含量的增加，(MoSiTiVZr)Nx高熵氮化物涂层的结构从无定形逐渐转变为单一的面心立方结构（FCC）。同时，涂层的晶粒尺寸、硬度、抗损伤性和耐磨性显著提升。当氮含量达到53.7 at.%时，涂层的最大硬度和杨氏模量分别达到45.6 GPa和408.2 GPa。所有测试的涂层均表现出优于304不锈钢的耐腐蚀性。然而，在氮含量为53.7 at.%时，由于晶粒尺寸增大和结构较为疏松，涂层的耐腐蚀性略低于对照组。涂层中的残余钼元素在腐蚀过程中对电子传导起到了积极作用。
This talk covers research background and current status of high-entropy alloy coatings with emphasis on (MoSiTiVZr)Nx high-entropy nitride coatings. Will illustrate that increase of N content leads to a structure change of the (MoSiTiVZr)Nx high-entropy nitride coatings from amorphous to single FCC. Meanwhile, the grain size, hardness, damage-tolerance and wear resistance significantly increase. The maximum hardness and Young’s modulus of the coating reaches 45.6 GPa and 408.2GPa, respectively at nitrogen content of 53.7 at.%. The corrosion resistance of all the coatings tested are better than that of 304 stainless steel. At 53.7 at.% N, the corrosion resistance of the coating is slightly inferior than that the control group mainly due to increase of grain size and loose structure. The residual Mo in the coating has a positive effect on the electron transport during the corrosion process.
报告人：张善勇（Sam Zhang）
报告人简介：
张善勇教授（Sam Zhang）现任薄膜学会主席，哈尔滨工业大学航天学院教授，哈尔滨工业大学郑州研究院教授。英国皇家化学学会会士（FRSC）、英国材料学会会士（FIoMMM）、国际薄膜学会会士（FTFS）。
张善勇教授于1982年获得东北大学材料学学士学位，1984年获得北京钢铁研究总院材料学硕士学位。1986年，赴美在威斯康星大学麦迪逊校区攻读博士，并于1991年获得材料学博士学位。1991年8月，加入新加坡南洋理工大学，并于2006年升任终身正教授。
2007年，张教授当选为英国材料学会会士（FIoMMM）。2009年，入选中国国家高层次人才计划，并受邀参加国庆60周年观礼。2018年，当选为英国皇家化学学会会士（FRSC）和国际薄膜学会会士（FTFS）。2018年1月，加入西南大学材料与能源学院，创建了“新薄膜材料与器件研究中心”，并担任中心主任。2023年，加盟哈尔滨工业大学。
张教授曾担任《Nanoscience and Nanotechnology Letters》的创刊主编（2008-2015），《Journal of Materials Research》与《Surface and Coatings Technology》期刊的编委，同时也是国际薄膜学会的创始人和现任会长/理事。
报告地点：上海大学宝山校区东区16号楼520会议室
报告时间：2024年11月5日（星期二）14：00
邀请人：王林军 教授